高性能重防腐用氟碳面漆的研制

张伟丽，李敏，徐科，方健君
（中海油常州涂料化工研究院有限公司，江苏常州 213016）

摘要：采用 3 种不同的氟树脂作为基料，通过改变 P/B 和 NCO/OH 配比，制备了不同的面漆配套板。 经
过对耐沸水性、耐酸碱性以及人工气候老化性能的对比研究，得出了高性能重防腐用氟碳面漆的制备参数。
关键词：氟树脂；高性能；氟碳面漆；制备参数
中图分类号：TQ630.7 文献标识码：A 文章编号：1672-2418(2019)07-0021-06

Preparation of High Performance Heavy-Duty Anti-

corrosive Fluorocarbon Topcoat

Zhang Weili, Li Min, Xu Ke, Fang Jianjun
(CNOOC Changzhou Paint and Coatings Industry Research Institute Co., Ltd., Changzhou 213016,
China)

Abstract: Different topcoats were prepared by using three different fluorocarbon resins as binders
at different ratios of the P/B and NCO/OH. The boiling water resistance, acid and alkali resistance
and artificial weathering performance of the topacoats were comparatively investigated. The optimal
parameters for preparing the high performance heavy-duty anticorrosive fluorocarbon topcoat were
obtained.
Keywords： fluorocarbon resins; high performance; fluorocarbon topcoat; preparation parameters

0 引言 得高键能的 C-F 键对低键能的 C-C 键起到了很好的
屏蔽和保护作用，能够很好地阻隔氧的渗透和紫外线
随着工业的高速发展，大型钢结构、海洋船舶、海 的破坏，从而提高了聚合物的整体性能 [3-4] 。
上设施和高层建筑对涂料的防腐蚀性以及耐久性等提 氟碳涂料作为一种超耐候涂料，其遵循的标准主
出了更高的要求。 由氟树脂制得的常温固化型氟碳涂 要为 HGT 3792—2014 《交联型氟树脂涂料》。 而在重

料，以其超常的耐候性、超强的耐腐蚀性和优异的耐化 防腐领域，由于应用环境更为苛刻，在使用过程中除
[1]
学药品性等特点，在重防腐领域得到了广泛的应用 。 了要满足以上标准，同时还要满足一些更高的性能要
氟树脂之所以具有如此优异的性能，主要取决于 求。 本研究选择了 3 种不同的氟树脂作为基体树脂，
聚合物中的氟原子，氟原子电负性高（4.0），原子半径 通过与异氰酸酯固化剂进行交联固化，探讨了不同氟
小 （0.135 nm），C-F 键极 短，键 能 高达 485 kJ/mol，分 树脂， 不同 P/B 和 NCO/OH 配比对漆膜耐性的影响。
[2]
子结构较其他结构具有更高的稳定性 。 而在相同结 从而研制出了满足 GB 50393—2008《钢制石油储罐防
构的氟树脂中，含氟量越高，树脂的性能越好。 另外， 腐蚀工程技术规范》中对氟碳类防腐蚀涂料性能要求
在氟树脂中， 氟原子紧密排列在 C-C 主链的周围，使 的高性能氟碳面漆。