高柔韧性环氧丙烯酸消光热转印粉末涂料

邓琨，巴旭民
（黄山华佳表面科技有限公司，安徽黄山，245061）

摘要：本研究旨在提高甲基丙烯酸缩水甘油酯（GMA）环氧基丙烯酸消光粉末涂料的耐冲击、抗划伤性
能，改善涂膜外观，解决了因不同体系相分离导致的“起花”、“亮点”缺陷，并将这一粉末涂料成功应用在不
锈钢防盗门上，解决了粉末涂料在不锈钢底材上的附着力不良问题。
关键词：GMA 消光；粉末涂料；不锈钢；附着力；热转印
中图分类号：TQ630.7 文献标识码：A 文章编号：1672-2418(2019)09-0019-04

High Flexibility GMA Matt Thermal Transfer Powder Coatings

Deng Kun, Ba Xumin

(Huangshan Huajia Surface Technology Co., Ltd., Huangshan, Anhui 245061, China)

Abstract: The purpose of this paper is to improve the impact resistance， scratch resistance and
film appearance of the glycidyl methylacrylate (GMA) epoxy acrylic matting powder coatings.
Meanwhile, the film defects such as floating and flashing due to phase separation are solved. The
powder coatings are used successfully in stainless steel security door wherein the adhesion of film on
the stainless steel substrate is improved.
Keywords： GMA matt； powder coatings； stainless steel； adhesion； thermal transfer

0 引言 类粉末涂料存在天生缺陷，如机械性能差，很难通过
50 cm 反冲， 表面耐划伤和耐磨性差， 表面容易起亮
传统热转印防盗门多采用门板成型后喷涂粉末 点、花纹等限制了其应用范围的拓展。
涂料再热转印的工艺， 由于门板上立体图案的影响，
转印工序阶段常出现凹槽内漏转或转印图案不清晰 1 实验部分
的缺陷。 新式施工采用整块平面门板喷涂粉末涂料再
1.1 主要原材料
通过热转印形成图案后，再根据需要对门板冲压成不
同形状的工艺，该种生产工艺的优点是可根据实际需 羧基封端聚酯树脂：工业级，神剑新材料。 环氧基
求冲压出不同的形状，且门板的转印图案清晰，丰满 丙烯酸消光树脂：工业级，宁波南海。 固化剂（TGIC）：
度好；缺点是后成型工艺中要使用例如冲床、折弯机、 工业级，黄山华惠。 颜料、填料、粉末涂料通用助剂（流
辊轧机等设备， 若涂层的抗冲击和柔韧性能不佳，就 平剂、安息香）、附着力促进剂、消除亮点或花纹助剂、
会出现爆边、起皮、脱落等缺陷。 热转印木纹纸：均为市售工业品。
环氧基丙烯酸消光粉末涂料可以实现＜10%的极
1.2 实验仪器和试验方法
致亚光效果，光泽稳定，且该体 系交 联 密度 大，易 撕
纸、转印图案清晰，广泛应用在热转印铝材领域。 但该 双螺杆挤出机；ACM 磨机；静电喷枪；烘箱；热转