预涂卷材用铁青灰面漆 QUV 抗老化性能改进

袁浩，常霞俊，濮靖，华涛，甘崇宁
（中海油常州涂料化工研究院有限公司，江苏常州 213016）

摘要：探讨了颜基比和黑色颜料对预涂卷材铁青灰面漆的老化性能的影响。 实验结果表明，颜基比对
铁青灰色卷材面漆的老化性能影响较大，颜基比越低，老化性越好；黑色颜料的密度和吸油量对铁青灰的
老化性能影响明显，其中铁黑的老化性最好。
关键词：预涂卷材涂料面漆；铁青灰； QUV；老化性能
+
中图分类号：TQ630.7 2 文献标识码：A 文章编号：1672-2418(2019)08-0017-04

Anti-Aging Modification of Iron Grey Precoated Coil
Topcoat

Yuan Hao , Chang Xiajun, Pu Jing, Hua Tao, Gan Chongning
(CNOOC Changzhou Paint and Coatings Industry Research Institute Co., Ltd, Changzhou, Jangsu
213016, China)

Abstract: The effects of pigment/binder ratio and black pigments on the anti-aging properties of
iron grey precoated coil topcoating were discussed. The experimental results showed that the
pigment/binder ratio had a great influence on the anti-aging properties of iron grey topcoatings.The
lower pigment/binder ratio could result in the better anti -aging properties of the topcoating. In
addition, the density and oil absorption of the black pigments had a significant influence on the
anti-aging properties of iron grey topcoat, wherein the iron black pigment showed the best anti-
aging performance.
Keywords： precoated coil topcoat; iron grey; QUV; anti-aging property

[2]
0 引言 牲部分性能降低漆膜厚度 ，卷材涂料长期暴露于户
外，要经受太阳光长期的辐射(主要是紫外光)、温度、
预涂卷材涂料在建筑板材方向有着重要的应用， 相对湿度和氧化的共同侵袭，这个复合作用使得涂膜
而建筑板材大多用在户外，耐久性能成为评价卷材涂 缓慢发生降解， 再加上户外逐年变化的恶劣气候，表
[1]
料的一项重要性能指标 。 在卷材涂料使用过程中暴 现为失光、变色或褪色、粉化、开裂等现象 。 卷材涂料
[3]
露出的较多问题中，粉化和失光等耐老化性能问题尤 的老化问题成为一个迫切需要解决的问题。 提高卷材
为突出。 失光带来建筑板材的光泽降低，粉化使得基 涂料的耐老化性能一方面可以提高产品的使用期限，
板裸露、生锈，减少使用寿命。 延长对基材的保护时间，另一方面可以降低涂料的使
伴随着卷材市场的发展，行业内部的竞争也日趋 用频率，减轻对环保的压力。