环氧丙烯酸改性水性醇酸树脂的合成研究

戴国绪，刘风广
（常州广树化工科技有限公司，江苏常州 213000）

摘要：通过实验选择亚麻油酸并确定油度为 35%~40%，选择松香和苯甲酸作为一元酸，和其他原料一
起反应制备醇酸树脂。 再用环氧酯树脂和丙烯酸酯类单体进行改性，最终确定当醇超量为 8%~10%、环氧
酯树脂加入量为 10%、丙烯酸加入量为 8%~10%时，制得的改性水性醇酸树脂的综合性能最佳。
关键词：醇酸树脂；环氧树脂；丙烯酸酯；化学改性；水性化
中图分类号：TQ630.7 文献标识码：A 文章编号：2096-8639(2020)07-0020-05

Synthesis of Waterborne Alkyd Resin Modified by Epoxy

Acrylic Acid !!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!

Dai Guoxu， Liu Fengguang
(Changzhou Guangshu Chemical Technology Co., Ltd., Changzhong, Jiangsu 213000, China)

Abstract: A linoleic acid was selected through experiments and its oil degree was determined to
be 35%-40%. Rosin and benzoic acid were selected as monoacid to react with other raw materials
to prepare an alkyd resin. After modification with epoxy resin and acrylate monomers, it is finally
determined that the comprehensive performance of the modified waterborne alkyd resin is the best
when the excess amount of alcohol is 8%-10%, the addition amount of epoxy resin is 10% and the
addition amount of acrylic acid is 8%-10%.
Keywords： alkyd; epoxy resin；acrylate；chemical modification; waterborne

0 引言 位。 醇酸树脂的水性化近年来也得到了越来越多的重
视和研究，但由于水性醇酸树脂涂料干燥慢、漆膜硬
在涂料工业环保化进程的不断推进中， 水性化、 度低、耐水差、不耐碱以及耐溶剂性差等缺点，因而在
高固化、 粉末化以及光固化是实现涂料产品绿色环 水性涂料市场并没有太多的竞争优势。 本研究通过复

保、涂料工业可持续发展的 4 大基本途径和方法。 在 合改性的方法制得了一种水性醇酸树脂， 其性能优
上述 4 大环保途径中， 水性化的方法具有工艺简便、 越，尤其是在干燥速度和耐水性方面已接近溶剂型醇
可实施性强、成本低、环保力度大等优势，因而在涂料 酸树脂涂料的水平。
工业绿色化过程中被普遍推崇，是实现环保涂料的最
常用的一种方法。 1 实验部分
醇酸树脂具有漆膜丰满、光泽高、附着力好、色彩
1.1 主要原材料
装饰性强等优点， 因此成为涂料工业中的骨干树脂，
在涂料领域尤其是工业涂料领域具有不可取代的地 主要原材料见表 1。

20 探索研究 RESEARCH AND DEVELOPMENT